RacingBrake Header H1 Image
  spacer
 Home RacingBrake.com  
General Information
    About Us
    Brake Technology
    F.A.Q.
    Feature Comparison
    Manufacturing
    Product Knowledge
Products
    Search by Category
Dealers
    Find a Dealer
    Become a Dealer
    Dealer Login
Media Center
    Gallery
    Magazines
    Testimonials
Forums
    General Discussion
    New Development
    Product Reviews
    Key Messages Posted
    Latest Topics
Support
    Careers
    Contact Us
    Privacy Policy
    Tech Tips
    Warranty Information

  Payments

 Payments

 

Go Back   RacingBrake Forums > Category > Key Messages Posted to Various Forums

Reply
 
Thread Tools Search this Thread Display Modes
Old 12-18-2006, 05:44 AM   #1
racingbrake
 
racingbrake's Avatar
 
Default RX7: RB Rotor Material

This reply was posted to RX7 forum on 12-16-2006 under this thread:
FD New Brake Options

Quote:
Wow, I never thought I'd see Howard wetting his pants over something like this...

No, you didn't.

BTW, most aftermarket 2-piece rotors use billet aluminum hats so this isn't exactly a new development...

Which is? Most rotors are made from cast iron. How are these any different? Cryo treated? High nickel content? What?

Sounds like this might be a better match for all the existing 13.0" (330mm) front brake kits than the 'RZ-spec' 12.4 x 0.8" (314 x 20mm) rear rotors available from Mazda and Precision Brakes... if it allows retaining the OEM parking brake and balances the piston area increase front to rear...

Having matching rotor diameters is not really the problem. It's the mismatch in the piston area ratio when upgrading to an aftermarket 4- or more-piston front caliper and retaining the stock rear calipers. Even the '99-spec rear calipers don't offer increased piston area. If they can fix that, then they've got something.
Hi, This is Warren from RacingBrake that Howard and Rishie are mentioning. Hello to everyone.

We got into this RX7 brake project through Howard?s inspiration and enthusiasm which means a lot to a relatively unknown brake company like us.

I admire the respect that Howard received from you folks and from my experience in working with him only about two weeks, the diligence and eagerness he demonstrated and the efforts he puts into this project and shared with other RX7 enthusiasts what he found proven that he is well deserved.

I have just noticed user jimlab #32 asked some questions which I like to reply as follows:


BTW, most aftermarket 2-piece rotors use billet aluminum hats so this isn't exactly a new development...

RB rotor hats are made (machined) from "Forged" aluminum blank in stead of cutting from billet (aluminum bar) which is "extruded" and readily available from aluminum mfgrs such as Alcoa or Kaiser. We have to make various "blank" tooling for different sizes of hat. This is not a new development rather it's a process that we all know costs more to make, yet has the benefit of better stiffness and strength than those made from billets that offered by most competitions. RB commits to performance brakes. More and more enthusiasts start to realize that our extra efforts are worthwhile.
http://www.racingbrake.com/main/two-...mbly.asp?i=hat

Which is? Most rotors are made from cast iron. How are these any different? Cryo treated? High nickel content? What?

RB rotors material are alloyed and heated from the base of SAE G3500 gray iron instead of G3000 which is the standard brake material for motor companies and aftermarket but unfortunately very few aftermarket brake meets this standard based on our past experience. Our rotors have higher carbon than regular gray iron for better heat handling but carbon will also weaken the strength of iron, so the alloys (Cu, Cr, Ni, Mo etc) may be added to make up the loss of strength resulting from the increase of carbon contents and enhance performance under extreme heat. But there are more important aspects than just the chemical compositions (% of elements) that predominately dictate the overall performance of a brake disc such as microstructure which deals with the formation (type and size) of graphite (carbon) and the matrix (distribution of pearlite or ferrite), that is beyond the scope of discussion here. Some reference link (scroll to Rotor Material)
http://www.racingbrake.com/main/rotor_is_important.asp

At RacingBrake we believe in the basic material science, therefore we like to heat treat our iron because when you hit the brake, the temperature surged, so we developed a process to heat up the casting higher than the highest brake temperature a rotor can reach, then cool it down. The discs are cut from these ?treated? casting which might have some sort of deformation that is not noticeable with eyes. You may consider this is a process similar to ?pre-warp? the rotors then machine from those ?warped? castings. This explains to our customers why RB rotors will not warp and are more resistant to wear and heat checks. More on heat treatment but again it?s beyond the scope of our discussion.

The above made us to disbelieve on Cryo treatment which some companies are marketing to teat the rotors on opposite way ? cool it down. We don?t have enough experience to comment on Cryo treatment but we know from the experience we had with those companies supplying brakes to professional racing teams (NASCAR) they only use heat-treated rotors, not Cryo.

Link to Cryogenic treatment question asked by an EVO racer
http://forums.racingbrake.com/viewto...highlight=cryo
racingbrake is offline   Reply With Quote
Old 12-19-2006, 11:56 AM   #2
racingbrake
 
racingbrake's Avatar
 
Default More questions on rotor material

Quote:
Originally Posted by whitey85mtu in RX7 under the same thread:

Quote:
When you form the pearlite, are you forming fine or corse pearlite? I'm only asking because like you said, adding more carbon will increase stregnth and hardness, but will reduce ductility and impact resistance, and that you are adding Cu, Cr, Ni, Mo, etc. to get back some ductility and impact resistance. I'm curious about the pearlite size because that will also affect dislocation movement, which for those who dont' know what that means, it affects ductility and hardness and toughness.
To clarify your question, if you read my earlier statement again you will realize; The carbon contents may be increased for better heat handling but at the cost of ?decreasing? the strength and hardness of an iron ? Not increase. Also the purpose of adding alloys is to make up (improve) the strength and thermal stability not the ductility.

Due to the graphite formation in gray iron is in flake shape therefore the gray iron although is excellent in thermal conductivity and ?damping? capacity which is like absorbing the vibration (make vibration less noticeable by the driver) but is ?not? as good in strength and impact resistance comparing to ductile iron which the graphite is in spherical shape. Ductile Iron has better strength due to it?s ductility and is a more suitable material for structural (stationary) members such as calipers and caliper brackets where no heat cycles are encountered like brake discs.

So an ideal cast iron for a brake rotor is to have the good thermal conductivity like gray iron (flake graphite) but with good strength as ductile iron (spherical graphite). It?s called Compacted Graphite Iron (CGI). It?s a relative new casting process and still is not very popular yet due to more difficult to produce and cost more to make. However RB does offer CGI rotors in some selective club racing applications. (We believe we are the first brake company introduces CGI rotors in performance brake industry.)

http://www.racingbrake.com/Club_Rac...tors_s/4338.htm

Racingbrake CGI rotors helped Tom Long won his North American Title on his Pro Spec Miata race.

http://forums.racingbrake.com/viewt...af4240938ba87fa

We prefer the fine pearlite matrix for better strength and hardness which make rotors more resistant to wear and heat handling.

Thank you for your questions.
racingbrake is offline   Reply With Quote
Reply


Thread Tools Search this Thread
Search this Thread:

Advanced Search
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

vB code is On
Smilies are On
[IMG] code is On
HTML code is On
Forum Jump


All times are GMT -7. The time now is 11:07 PM.
View Forum Archive.
Powered by vBulletin® Version 3.6.8
Copyright ©2000 - 2017, Jelsoft Enterprises Ltd.
   
  TPM Products Inc. Copyright 1985 - 2009 TPM Products, Inc. TPM® and RacingBrake are our trademarks.
1556 Kimberly Avenue, Fullerton, CA 92831, Phone: 714-871-6392 Fax: 714-871-9736